国外阀门材料常用技术标准 镍合金锻件化学要求（2）
| 成分，（%） | |||||||||
| 元素 | 镍-铁-铬 合金 UNS N08811 | 镍-铬-钼-铌 合金 UNS N06625 | 镍-铬-钼-钨 合金 UNS N06110 | 镍-铁-铬- 钼-铜合金 UNS N08825 | 低碳镍-钼- 铬合金 UNS N10276 | 低碳镍-钼- 铬合金 UNS N06022 | 铁-镍-铬-钼 -氮合金 UNS N08367 | 低碳镍-铬- 钼合金 UNS N06059 | 低碳镍-铬- 钼合金 UNS N06058 |
| 镍 | 30.0-35.0 | ≥58.0A | ≥51.0A | 38.0-46.0 | 残留元素A | 残留元素A | 23.50-25.50 | 平衡A | 平衡 |
| 铜 | ≤0.75 | … | ≤0.50 | 1.5-3.0 | … | … | ≤0.75 | ≤0.50 | ≤0.50 |
| 铁 | ≥39.5A | ≤5.0 | ≤1.0 | ≥22.0 | 4.0-7.0 | 2.0-6.0 | 残留元素A | ≤1.5 | ≤1.5 |
| 锰 | ≤1.5 | ≤0.5 | ≤1.0 | ≤1.0 | ≤1.0 | ≤0.50 | ≤2.00 | ≤0.5 | ≤0.50 |
| 碳 | 0.06-0.10 | ≤0.10 | ≤0.15 | ≤0.05 | ≤0.010 | ≤0.015 | ≤0.030 | ≤0.010 | ≤0.010 |
| 硅 | ≤1.0 | ≤0.5 | ≤1.0 | ≤0.5 | ≤0.08 | ≤0.08 | ≤1.00 | ≤0.10 | ≤0.10 |
| 硫，≤ | 0.015 | 0.015 | 0.015 | 0.03 | 0.03 | 0.02 | 0.030 | 0.010 | 0.010 |
| 铬 | 19.0-23.0 | 20.0-23.0 | 28.0-33.0 | 19.5-23.5 | 14.5-16.5 | 20.0-22.5 | 20.0-22.0 | 22.0-24.0 | 20.0-23.0 |
| 铝 | 0.15-0.60 | ≤0.4 | ≤1.0 | ≤0.2 | … | … | … | 0.1-0.4 | ≤0.40 |
| 钛 | 0.15-0.60 | ≤0.4 | ≤1.0 | 0.6-1.2 | — | … | … | … | … |
| 铌+钽 | … | 3.15-4.15 | ≤1.0 | … | — | … | … | … | … |
| 钼 | … | 8.0-10.0 | 9.0-12.0 | 2.5-3.5 | 15.0-17.0 | 12.5-14.5 | 6.00-7.00 | 15.0-16.5 | 19.0-21.0 |
| 磷 | … | ≤0.015 | ≤0.50 | … | ≤0.04 | ≤0.02 | ≤0.040 | ≤0.015 | ≤0.015 |
| 钨 | … | … | 1.0-4.0 | … | 3.0-4.5 | 2.5-3.5 | … | … | ≤0.3 |
| 钴 | … | … | … | … | ≤2.5 | ≤2.5 | … | ≤0.3 | ≤0.3 |
| 钒，≤ | … | … | … | … | 0.35 | 0.35 | … | … | … |
| 氮 | … | … | … | … | … | … | 0.18-0.25 | … | 0.02-0.15 |
| 硼 | … | … | … | … | … | … | … | … | … |
| 镧 | … | … | … | … | … | … | … | … | … |
| 铝+钛 | 0.85-1.20 | … | … | … | … | … | … | … | … |
| 镍+钼 | … | … | … | … | … | … | … | … | … |
| 铌，≤ | … | … | … | … | … | … | … | … | … |
| 钽 | … | … | … | … | … | … | … | … | … |
| 锆，≤ | … | … | … | … | … | … | … | … | … |
| 铈 | … | … | … | … | … | … | … | … | … |
| 钇 | … | … | … | … | … | … | … | … | … |